Husaini, Mitsuo Notomi, Kikuo Kishimoto, Toshikazu Shibuya
Mode I and mixed mode loading testing of ABS resin were carried out by using compact tension shear specimens. Two types of ABS resin were examined. The first one (ABS-1) has a butadiene rubber content of 18 wt % in the form of small particles of diameter of about 200 nm. The second one (ABS-2) has the same overall butadiene rubber content but a bimodal particle distribution with diameters of 200 nm and 500 nm. Crack initiation behavior was observed by using a video microscope. The fracture toughness of ABS-2 obtained by mode I testing is larger than that of ABS-1. The fracture angle for both materials under mixed mode loading coincides with the values predicted by the maximum hoop stress criterion. On the contrary, at crack initiation under mixed mode loading, the critical values of KI and KII are larger than those estimated by the maximum hoop stress criterion. The increase in the critical values of KI and KII under mixed mode loading for ABS-2 is higher than those for ABS-1. The bimodal type distribution of rubber particle size produces better fracture resistance.
Department of Mechanical Engineering, Faculty of Engineering, Syiah Kuala University, Darussalam-Banda Aceh 23111, Indonesia; Dept. Mech. Intelligent Syst. Eng., Tokyo Institute of Technology, O-okayama, Meguro-ku, Tokyo 152, Japan
Research at a Glance
Register to unlock
Topics & SDG Alignment
Register to unlock
Collaboration
Register to unlock
Author Profile (Selected)
Register to unlock
References Overview
Register to unlock
Journal & Source
Register to unlock
Metadata & Integrity
Register to unlock