S. Rizal, H. Homma, M. Nazer, E. Kishida
Dimple fracture mechanisms are discussed for three kinds of aluminum alloys on the basis of an experimental approach and a finite element (FEM) analysis. The void growth and coalescence process was observed by an optical microscope and a scanning electron microscope. The fractographic observation for aluminum alloys 7075-T651 and 6061-T651 showed that several large voids called a dominant void are nucleated at inclusion sites or the second-phase particles ahead of the crack tip and followed by fine voids initiation leading coalescence of the dominant voids with the crack tip. On the other hand, in aluminum alloy 2017-T3, voids are nucleated very close to the crack tip and directly coalesce with the crack tip. FEM computation results suggested that the void nucleation and growth process is closely related to the triaxial stress state ahead of the crack tip. © 2002 Elsevier Science Ltd. All rights reserved.
Department of Mechanical Engineering, Research Center for Evaluation and Prevention Failure of Materials, Syiah Kuala University, Darussalam-Banda Aceh 23111, Indonesia; International Cooperation Center for Engineering Education Development, Toyohashi University of Technology, Toyohashi 441-8540, 1-1 Hibarigaoka, Tempaku-cho, Japan
Research at a Glance
Register to unlock
Topics & SDG Alignment
Register to unlock
Collaboration
Register to unlock
Author Profile (Selected)
Register to unlock
References Overview
Register to unlock
Journal & Source
Register to unlock
Metadata & Integrity
Register to unlock